The paper presents the effect of vanadium addition to aluminum and aluminum grain refined by titanium on the micron level, in the range from 0.005 wt % to 0.236 wt %, on their corrosion resistance in acidic solution, HCl, at three different temperatures namely: 25 degrees C, 40 degrees C and 60 degrees C. It was found that the corrosion rate was slightly increased by the addition of any percentage of vanadium at 25 degrees C. Furthermore, it was found that the corrosion rate increased with the increase of temperature at any percentage of vanadium addition in the case of both aluminum and aluminum grain refined by titanium. However it was found that addition of vanadium at any percentage to either aluminum or aluminum+ titanium, resulted in decrease of the corrosion rate i.e. improvement in their corrosion resistance in acidic solution at 40 degrees C and 60 degrees C. The maximum achieved reduction in corrosion rate was 77 % at 40 degrees C and 0.148 wt % vanadium addition.https://www.researchgate.net/publication/272486506_Effect_of_Vanadium_Addition_to_Aluminum_and_Aluminum_Grain_Refined_by_Titanium_on_Their_Chemical_Corrosion_Rate_in_Acidic_Solution_HCl_at_Different_Temperatures
The paper presents the effect of vanadium addition to aluminum and aluminum grain refined by titanium on the micron level, in the range from 0.005 wt % to 0.236 wt %, on their corrosion resistance in acidic solution, HCl, at three different temperatures namely: 25 degrees C, 40 degrees C and 60 degrees C. It was found that the corrosion rate was slightly increased by the addition of any percentage of vanadium at 25 degrees C. Furthermore, it was found that the corrosion rate increased with the increase of temperature at any percentage of vanadium addition in the case of both aluminum and aluminum grain refined by titanium. However it was found that addition of vanadium at any percentage to either aluminum or aluminum+ titanium, resulted in decrease of the corrosion rate i.e. improvement in their corrosion resistance in acidic solution at 40 degrees C and 60 degrees C. The maximum achieved reduction in corrosion rate was 77 % at 40 degrees C and 0.148 wt % vanadium addition.
https://www.researchgate.net/publication/272486506_Effect_of_Vanadium_Addition_to_Aluminum_and_Aluminum_Grain_Refined_by_Titanium_on_Their_Chemical_Corrosion_Rate_in_Acidic_Solution_HCl_at_Different_Temperatures
17.Apr.2024
16.Jan.2024
20.Sep.2023
أنا طالبة في الهندسة الصناعية, اختياري لهذا التخصص كان بناءً على أهميته الكبيرة كمهنة في الحاضر والمستقبل ... رغد بركات
الهندسة الصناعية تساعدك على اتخاذ قرارات أفضل، وتعطي أشكالا أخرى من مبادئ الهندسة بشكل عملي وعلمي في آن. ... محمود صلاح
قسم الهندسة الكيميائية قسم جميل جدا تعلمت فيه الكثير ومما تعلمته فيه جدية العمل وروح الفريق الواحد .. ... رغد الشويكي